YT62 TORAYFAN*

Features

A biaxially oriented polypropylene film which can be easily torn open by hand in the lateral direction, and in a straight line.

(1)Easy to tear by hand straightly in transversal direction if used in single layer. Laminated film or bag had better be notched.
(2)Excellent processabilty for printing and lamination as same as general OPP films.

Thickness

40µm

Typical properties

Properties Unit
Direction
/Side
Typical Data Measurement method
Thickness µm   40  
Tensile strength MPa MD 60 JIS Z1712
TD 330
Elongation at break % MD 170 JIS Z1712
TD 40
Young's Modules GPa MD 1.5 ASTM D882-64T
TD 3.0
Thermal Shrinkage
(120°C15 min.)
% MD 1.0 JIS Z1712
TD 0.0
Coefficient of Friction(µs/µd) - inner side 0.35/0.30 Toray method
outer side 0.25/0.20
Surface wetting tension mN/m inner side 39 JIS Z1712
outer side 38
Surface Resistivity LogΩEcm inner side 13 Toray method
outer side 11
Sharpy Impact Strength MJ/m² TD 1.8 Toray method
Curl Rate(ordinary temperature rate) % MD 30 Toray method
Curl Rate(100°C3 min.) % TD 50 Toray method

*Atomospheric Condition 25°C65%RH

Applications

Adhesive tape etc.

Attention
1. We accept no responsibility for results obtained by the application of the information indicated and for the safety and suitability of the products, by itself or in combination with other products. Users are advised to perform their own tests to determine the safety and suitability of such product and product combinationaccording to each of its purposes.
2. Refer to our MSDS (Material Safety Data Sheet) before use.
3. The publication is not to be taken as a license to operate under, or as a recommendation to infringe any patents.
  • Back
  • Print Friendly Page

PAGE TOP

  • Terms of use
  • Privacy Policy
  • Site map

YT62 TORAYFAN*

TORAYFAN*

Features

A biaxially oriented polypropylene film which can be easily torn open by hand in the lateral direction, and in a straight line.

(1)Easy to tear by hand straightly in transversal direction if used in single layer. Laminated film or bag had better be notched.
(2)Excellent processabilty for printing and lamination as same as general OPP films.

Thickness

40µm

Typical properties

Properties Unit
Direction
/Side
Typical Data Measurement method
Thickness µm   40  
Tensile strength MPa MD 60 JIS Z1712
TD 330
Elongation at break % MD 170 JIS Z1712
TD 40
Young's Modules GPa MD 1.5 ASTM D882-64T
TD 3.0
Thermal Shrinkage
(120°C15 min.)
% MD 1.0 JIS Z1712
TD 0.0
Coefficient of Friction(µs/µd) - inner side 0.35/0.30 Toray method
outer side 0.25/0.20
Surface wetting tension mN/m inner side 39 JIS Z1712
outer side 38
Surface Resistivity LogΩEcm inner side 13 Toray method
outer side 11
Sharpy Impact Strength MJ/m² TD 1.8 Toray method
Curl Rate(ordinary temperature rate) % MD 30 Toray method
Curl Rate(100°C3 min.) % TD 50 Toray method

*Atomospheric Condition 25°C65%RH

Applications

Adhesive tape etc.

Attention
1. We accept no responsibility for results obtained by the application of the information indicated and for the safety and suitability of the products, by itself or in combination with other products. Users are advised to perform their own tests to determine the safety and suitability of such product and product combinationaccording to each of its purposes.
2. Refer to our MSDS (Material Safety Data Sheet) before use.
3. The publication is not to be taken as a license to operate under, or as a recommendation to infringe any patents.

Print