YM17S TORAYFAN*

Features

A biaxially oriented polypropylene film with matte finish on one side.

1)With a highly matte tone, a subdued, sophisticated surface appearance can be achieved.
2)Both sides of the film are excellent in mold release property.

Thickness

20,25µm

Typical properties

Properties Unit
Direction
/Side
Typical Data Measurement method
Tensile Strength MPa MD 100 JIS Z1712
TD 230
Elongation at Break % MD 200 JIS Z1712
TD 60
Young's Modulus GPa MD 1.47 ASTM D882-64T
TD 2.75
Thermal Shrinkage
(140°C 15min)
% MD 8.0 JIS Z1712
TD 3.5
Haze % - 70 JIS Z1712
Light Transmittance % - 88 JIS K6714
Gloss(60°- 60°) % outer side 10 JIS K8741
Coefficient of Friction(µs/µd) - inner side/
inner side
0.25/0.20 Toray Method
outer side/
outer side
0.40/0.30
Surface Wetting Tension mN/m inner side 38 JIS Z1712
outer side 32
Surface Resistivity LogΩ • cm inner side 13 Toray Method
outer side 18

*Atomospheric Condition 25°C65%RH

Applications

Matte type for mold release, Packaging

Attention
1. We accept no responsibility for results obtained by the application of the information indicated and for the safety and suitability of the products, by itself or in combination with other products. Users are advised to perform their own tests to determine the safety and suitability of such product and product combinationaccording to each of its purposes.
2. Refer to our MSDS (Material Safety Data Sheet) before use.
3. The publication is not to be taken as a license to operate under, or as a recommendation to infringe any patents.
  • Back
  • Print Friendly Page

PAGE TOP

  • Terms of use
  • Privacy Policy
  • Site map

YM17S TORAYFAN*

TORAYFAN*

Features

A biaxially oriented polypropylene film with matte finish on one side.

1)With a highly matte tone, a subdued, sophisticated surface appearance can be achieved.
2)Both sides of the film are excellent in mold release property.

Thickness

20,25µm

Typical properties

Properties Unit
Direction
/Side
Typical Data Measurement method
Tensile Strength MPa MD 100 JIS Z1712
TD 230
Elongation at Break % MD 200 JIS Z1712
TD 60
Young's Modulus GPa MD 1.47 ASTM D882-64T
TD 2.75
Thermal Shrinkage
(140°C 15min)
% MD 8.0 JIS Z1712
TD 3.5
Haze % - 70 JIS Z1712
Light Transmittance % - 88 JIS K6714
Gloss(60°- 60°) % outer side 10 JIS K8741
Coefficient of Friction(µs/µd) - inner side/
inner side
0.25/0.20 Toray Method
outer side/
outer side
0.40/0.30
Surface Wetting Tension mN/m inner side 38 JIS Z1712
outer side 32
Surface Resistivity LogΩ • cm inner side 13 Toray Method
outer side 18

*Atomospheric Condition 25°C65%RH

Applications

Matte type for mold release, Packaging

Attention
1. We accept no responsibility for results obtained by the application of the information indicated and for the safety and suitability of the products, by itself or in combination with other products. Users are advised to perform their own tests to determine the safety and suitability of such product and product combinationaccording to each of its purposes.
2. Refer to our MSDS (Material Safety Data Sheet) before use.
3. The publication is not to be taken as a license to operate under, or as a recommendation to infringe any patents.

Print