YM11 TORAYFAN*

Features

YM11 is a biaxially oriented polypropylene film with matte finish on one side.

1)With a high matte tone, a subdued, sophisticated surface appearance can be achieved.
2)Both sides of the film are excellent in anti-static property.

Thickness

15,20µm

Typical properties

Properties Unit
Direction
/Side
Typical Data Measurement method
Tensile Strength MPa MD 100 JIS Z1712
TD 230
Elongation at Break % MD 200 JIS Z1712
TD 60
Young's Modulus GPa MD 1.47 ASTM D882-64T
TD 2.75
Thermal Shrinkage
(140°C 15min)
% MD 8.0 JIS Z1712
TD 3.5
Haze % - 70 JIS Z1712
Light Transmittance % - 88 JIS K6714
Gloss(60°- 60°) % outer side 10 JIS K8741
Coefficient of Friction(µs/µd) - inner side/
inner side
0.25/0.20 Toray Method
outer side/
outer side
0.25/0.20
Surface Wetting Tension mN/m inner side 39 JIS Z1712
outer side 41
Surface Resistivity LogΩ • cm inner side 12 Toray Method
outer side 12

*Atomospheric Condition:25°C65%RH

Applications

Packages (for Japanese and Western sweets, dry snack food, soap, etc.)
Examples of lamination:
YM11 (matte surface/gloss surface)/printing/CPP, PE
YM11 (ditto)/printing 1 metallized sealant
YM11 (ditto)/printing glue/pearl-tone film
For surface matte finishing(lined with printing paper)

Attention
1. We accept no responsibility for results obtained by the application of the information indicated and for the safety and suitability of the products, by itself or in combination with other products. Users are advised to perform their own tests to determine the safety and suitability of such product and product combinationaccording to each of its purposes.
2. Refer to our MSDS (Material Safety Data Sheet) before use.
3. The publication is not to be taken as a license to operate under, or as a recommendation to infringe any patents.
  • Back
  • Print Friendly Page

PAGE TOP

  • Terms of use
  • Privacy Policy
  • Site map

YM11 TORAYFAN*

TORAYFAN*

Features

YM11 is a biaxially oriented polypropylene film with matte finish on one side.

1)With a high matte tone, a subdued, sophisticated surface appearance can be achieved.
2)Both sides of the film are excellent in anti-static property.

Thickness

15,20µm

Typical properties

Properties Unit
Direction
/Side
Typical Data Measurement method
Tensile Strength MPa MD 100 JIS Z1712
TD 230
Elongation at Break % MD 200 JIS Z1712
TD 60
Young's Modulus GPa MD 1.47 ASTM D882-64T
TD 2.75
Thermal Shrinkage
(140°C 15min)
% MD 8.0 JIS Z1712
TD 3.5
Haze % - 70 JIS Z1712
Light Transmittance % - 88 JIS K6714
Gloss(60°- 60°) % outer side 10 JIS K8741
Coefficient of Friction(µs/µd) - inner side/
inner side
0.25/0.20 Toray Method
outer side/
outer side
0.25/0.20
Surface Wetting Tension mN/m inner side 39 JIS Z1712
outer side 41
Surface Resistivity LogΩ • cm inner side 12 Toray Method
outer side 12

*Atomospheric Condition:25°C65%RH

Applications

Packages (for Japanese and Western sweets, dry snack food, soap, etc.)
Examples of lamination:
YM11 (matte surface/gloss surface)/printing/CPP, PE
YM11 (ditto)/printing 1 metallized sealant
YM11 (ditto)/printing glue/pearl-tone film
For surface matte finishing(lined with printing paper)

Attention
1. We accept no responsibility for results obtained by the application of the information indicated and for the safety and suitability of the products, by itself or in combination with other products. Users are advised to perform their own tests to determine the safety and suitability of such product and product combinationaccording to each of its purposes.
2. Refer to our MSDS (Material Safety Data Sheet) before use.
3. The publication is not to be taken as a license to operate under, or as a recommendation to infringe any patents.

Print