VL10/VL12/VL22 TORAYFAN*

Features

The series of products are OPP film for thermal lamination applications, with tie resin applied by extrusion lamination as the adhesive layer.
VL10•VL12 are gross type,(VL10:OPP side non-treated,VL12:OPP side corona treated)
VL22 is matte type.

1)This series of films can be laminated together with paper in hot roll.(As adhesive layer is already provided, bonding agent does not need to be applied)
2)Excellent gloss and shine compared to solvent type.
3)Due to the absence of solvent, it is environmentally friendly.

Thickness

30µm

Typical properties

Properties Unit
Direction
/Side
VL10 VL12 VL22 Measurement method
Tensile strength MPa MD 70 70 60 JIS Z1712
TD 150 150 110
Elongation at break % MD 160 160 240 JIS Z1712
TD 50 50 50
Thermal Shrinkage
(120°C15 min.)
% MD 4.0 4.0 3.0 JIS Z1712
TD 2.0 2.0 1.0

Coefficient of Friction

(µs/µd)
- outer side/
outer side
0.35/0.30 0.25/0.20 0.20/0.20 Toray method
Surface wetting tension mN/m inner side 45 45 45 JIS Z1712
outer side 30> 35 37

*Atomospheric Condition:25°C65%RH
VL10:outer side:not treated/inner side for heat lamination
VL12:outer side:corona treated/inner side for heat lamination
VL22:outer side:matte, corona treated/inner side for heat lamination

Conditions for heat lamination

  Unit Recommended conditions

Heat

Roll Temperature
°C 90 - 120
Pressure kg/cm 30<
Speed M/ min. 20 - 50

Applications

1)Cover for various publications, books, and textbooks.
2)Carrying bags
3)Jacket covers for bc and DVD.
4)Boxes for cosmetic products
5)Paper containers for other daily-life commodities

Attention
1. We accept no responsibility for results obtained by the application of the information indicated and for the safety and suitability of the products, by itself or in combination with other products. Users are advised to perform their own tests to determine the safety and suitability of such product and product combinationaccording to each of its purposes.
2. Refer to our MSDS (Material Safety Data Sheet) before use.
3. The publication is not to be taken as a license to operate under, or as a recommendation to infringe any patents.
  • Back
  • Print Friendly Page

PAGE TOP

  • Terms of use
  • Privacy Policy
  • Site map

VL10/VL12/VL22 TORAYFAN*

TORAYFAN*

Features

The series of products are OPP film for thermal lamination applications, with tie resin applied by extrusion lamination as the adhesive layer.
VL10•VL12 are gross type,(VL10:OPP side non-treated,VL12:OPP side corona treated)
VL22 is matte type.

1)This series of films can be laminated together with paper in hot roll.(As adhesive layer is already provided, bonding agent does not need to be applied)
2)Excellent gloss and shine compared to solvent type.
3)Due to the absence of solvent, it is environmentally friendly.

Thickness

30µm

Typical properties

Properties Unit
Direction
/Side
VL10 VL12 VL22 Measurement method
Tensile strength MPa MD 70 70 60 JIS Z1712
TD 150 150 110
Elongation at break % MD 160 160 240 JIS Z1712
TD 50 50 50
Thermal Shrinkage
(120°C15 min.)
% MD 4.0 4.0 3.0 JIS Z1712
TD 2.0 2.0 1.0

Coefficient of Friction

(µs/µd)
- outer side/
outer side
0.35/0.30 0.25/0.20 0.20/0.20 Toray method
Surface wetting tension mN/m inner side 45 45 45 JIS Z1712
outer side 30> 35 37

*Atomospheric Condition:25°C65%RH
VL10:outer side:not treated/inner side for heat lamination
VL12:outer side:corona treated/inner side for heat lamination
VL22:outer side:matte, corona treated/inner side for heat lamination

M~

  Unit Recommended conditions

Heat

Roll Temperature
°C 90 - 120
Pressure kg/cm 30<
Speed M/ min. 20 - 50

Applications

1)Cover for various publications, books, and textbooks.
2)Carrying bags
3)Jacket covers for bc and DVD.
4)Boxes for cosmetic products
5)Paper containers for other daily-life commodities

Attention
1. We accept no responsibility for results obtained by the application of the information indicated and for the safety and suitability of the products, by itself or in combination with other products. Users are advised to perform their own tests to determine the safety and suitability of such product and product combinationaccording to each of its purposes.
2. Refer to our MSDS (Material Safety Data Sheet) before use.
3. The publication is not to be taken as a license to operate under, or as a recommendation to infringe any patents.

Print