NL10/NL12/NL22/NL82 TORAYFAN*

Features

The series of products are OPP films for thermal lamination applications, with EVA resin applied by extrusion lamination as the adhesive layer.
NL10 and NL12 are glossy types (NL10fs OPP surface is not treated, and NL12 has its OPP surface corona treated), NL22 is matte, and NL82 is glue-receptive.

1)This series of films can be laminated together with paper in hot roll(as adhesive layer is already provided, bonding agent does not need to be applied)
2)Excellent gloss and shine compared to solvent type.
3)Due to the absence of solvent, it is environmentally friendly.

Thickness

27.5µm

Typical properties

Properties Unit
Direction
/Side
NL10 NL12 NL22 NL82 Measurement method
Tensile Strength MPa MD 80 80 60 85 JIS Z1712
TD 170 170 110 185
Elongation at Break % MD 160 160 240 200 JIS Z1712
TD 50 50 50 50
Thermal Shrinkage
( 120°C 15min)
% MD 4.0 4.0 3.0 4.0 JIS Z1712
TD 2.0 2.0 1.0 3.0
Coefficient of Friction(µs/µd) - outer side/
outer side
0.35/0.30 0.25/0.20 0.20/0.20 0.25/0.20 Toray Method
Surface Wetting Tension mN/m inner side 45 45 45 45 JIS Z1712
outer side 30> 35 37 41

*Atomospheric Condition:25°C65%RH
NL10:outer side not treated/inner side for heat lamination
NL12:outer side corona treated/inner side for heat lamination
NL22:outer side matte, corona treated/inner side for heat lamination
NL82:outer side provides good adhesion/inner side for heat lamination

Condition for heat lamination

  Unit Recommended conditions
Heat Roll Temperature °C 100 - 120
Pressure kg/cm 30<
Web Speed & Lamination Process m/min 20 - 40

Applications

1)Cover for various publications, books, and textbooks.
2)Carrying bags
3)Jacket covers for CD and DVD.
4)Boxes for cosmetic products
5)Paper containers for other daily-life commodities.

Attention
1. We accept no responsibility for results obtained by the application of the information indicated and for the safety and suitability of the products, by itself or in combination with other products. Users are advised to perform their own tests to determine the safety and suitability of such product and product combinationaccording to each of its purposes.
2. Refer to our MSDS (Material Safety Data Sheet) before use.
3. The publication is not to be taken as a license to operate under, or as a recommendation to infringe any patents.
  • Back
  • Print Friendly Page

PAGE TOP

  • Terms of use
  • Privacy Policy
  • Site map

L10/NL12/NL22/NL82 TORAYFAN*

TORAYFAN*

Features

The series of products are OPP films for thermal lamination applications, with EVA resin applied by extrusion lamination as the adhesive layer.
NL10 and NL12 are glossy types (NL10fs OPP surface is not treated, and NL12 has its OPP surface corona treated), NL22 is matte, and NL82 is glue-receptive.

1)This series of films can be laminated together with paper in hot roll(as adhesive layer is already provided, bonding agent does not need to be applied)
2)Excellent gloss and shine compared to solvent type.
3)Due to the absence of solvent, it is environmentally friendly.

Thickness

27.5µm

Typical properties

Properties Unit
Direction
/Side
NL10 NL12 NL22 NL82 Measurement method
Tensile Strength MPa MD 80 80 60 85 JIS Z1712
TD 170 170 110 185
Elongation at Break % MD 160 160 240 200 JIS Z1712
TD 50 50 50 50
Thermal Shrinkage
( 120°C 15min)
% MD 4.0 4.0 3.0 4.0 JIS Z1712
TD 2.0 2.0 1.0 3.0
Coefficient of Friction(µs/µd) - outer side/
outer side
0.35/0.30 0.25/0.20 0.20/0.20 0.25/0.20 Toray Method
Surface Wetting Tension mN/m inner side 45 45 45 45 JIS Z1712
outer side 30> 35 37 41

*Atomospheric Condition:25°C65%RH
NL10:outer side not treated/inner side for heat lamination
NL12:outer side corona treated/inner side for heat lamination
NL22:outer side matte, corona treated/inner side for heat lamination
NL82:outer side provides good adhesion/inner side for heat lamination

Condition for heat lamination

  Unit Recommended conditions
Heat Roll Temperature °C 100 - 120
Pressure kg/cm 30<
Web Speed & Lamination Process m/min 20 - 40

Applications

1)Cover for various publications, books, and textbooks.
2)Carrying bags
3)Jacket covers for CD and DVD.
4)Boxes for cosmetic products
5)Paper containers for other daily-life commodities.

Attention
1. We accept no responsibility for results obtained by the application of the information indicated and for the safety and suitability of the products, by itself or in combination with other products. Users are advised to perform their own tests to determine the safety and suitability of such product and product combinationaccording to each of its purposes.
2. Refer to our MSDS (Material Safety Data Sheet) before use.
3. The publication is not to be taken as a license to operate under, or as a recommendation to infringe any patents.

Print