2578 TORAYFAN*

Features

2578 is general-purpose biaxially oriented polypropylene film with corona discharge treatment on one side.

1)Excellent in transparency.
2)One side is treated corona discharge, the other (non-treated) side is proofed against backside treatment.

Thickness

15,25,30,40µm

Typical properties

Properties Unit
Direction
/Side
Typical Data Measurement method
Tensile Strength MPa MD 150 JIS Z1712
TD 320
Elongation at Break % MD 180 JIS Z1712
TD 50
Thermal Shrinkage
(120°C 15min)
% MD 4.0 JIS Z1712
TD 1.0
Haze(1 sheet) % - 2 JIS Z1712
Coefficient of Friction(µs/µd) - inner side/
inner side
0.25/0.20 Toray Method
outer side/
outer side
0.35/0.30
Surface Wetting Tension mN/m inner side 38 JIS Z1712
outer side 30>
Surface Resistivity LogΩ • cm inner side 11.5 Toray Method
outer side/
outer side
-
Bubble piece/m² - 0 Toray Method
Penetrate through - outer side None Toray Method

*Atomospheric Condition:25°C65%RH

Applications

Lamination, bar code, print lamination (solvent bonding), releasing

Attention
1. We accept no responsibility for results obtained by the application of the information indicated and for the safety and suitability of the products, by itself or in combination with other products. Users are advised to perform their own tests to determine the safety and suitability of such product and product combinationaccording to each of its purposes.
2. Refer to our MSDS (Material Safety Data Sheet) before use.
3. The publication is not to be taken as a license to operate under, or as a recommendation to infringe any patents.
  • Back
  • Print Friendly Page

PAGE TOP

  • Terms of use
  • Privacy Policy
  • Site map

2578 TORAYFAN*

TORAYFAN*

Features

2578 is general-purpose biaxially oriented polypropylene film with corona discharge treatment on one side.

1)Excellent in transparency.
2)One side is treated corona discharge, the other (non-treated) side is proofed against backside treatment.

Thickness

15,25,30,40µm

Typical properties

Properties Unit
Direction
/Side
Typical Data Measurement method
Tensile Strength MPa MD 150 JIS Z1712
TD 320
Elongation at Break % MD 180 JIS Z1712
TD 50
Thermal Shrinkage
(120°C 15min)
% MD 4.0 JIS Z1712
TD 1.0
Haze(1 sheet) % - 2 JIS Z1712
Coefficient of Friction(µs/µd) - inner side/
inner side
0.25/0.20 Toray Method
outer side/
outer side
0.35/0.30
Surface Wetting Tension mN/m inner side 38 JIS Z1712
outer side 30>
Surface Resistivity LogΩ • cm inner side 11.5 Toray Method
outer side/
outer side
-
Bubble piece/m² - 0 Toray Method
Penetrate through - outer side None Toray Method

*Atomospheric Condition:25°C65%RH

Applications

Lamination, bar code, print lamination (solvent bonding), releasing

Attention
1. We accept no responsibility for results obtained by the application of the information indicated and for the safety and suitability of the products, by itself or in combination with other products. Users are advised to perform their own tests to determine the safety and suitability of such product and product combinationaccording to each of its purposes.
2. Refer to our MSDS (Material Safety Data Sheet) before use.
3. The publication is not to be taken as a license to operate under, or as a recommendation to infringe any patents.

Print