2548 TORAYFAN*

Features

A biaxially oriented polypropylene film, both sides treated with corona discharge and having strong anti-static property.

1)Both sides of film excel in anti-static property .Best suited to uses in packaging for powder products.
2)As both sides have been treated with corona discharge, when it is processed into bags, the outer side of the bag will have superior adhesion property thus can be easily marked with data stamps and other marks.
3)The strength of the biaxially oriented polypropylene film and the corona discharge treatment given on both sides makes 2548 ideal for use in adhesive tapes.

Thickness

20,25,30,40,60µm

Typical properties

Properties Unit
Direction
/Side
Typical Data Measurement method
Tensile Strength MPa MD 140 JIS Z1712
TD 300
Elongation at Break % MD 190 JIS Z1712
TD 60
Young's Modulus GPa MD 1.8 ASTM D882-64T
TD 3.4
Thermal Shrinkage
(120°C 15min)
% MD 3.5 JIS Z1712
TD 0.0
Haze % - 2 JIS Z1712
Coefficient of Friction
(µs/µd)
- inner side/
inner side
0.25/0.20 Toray Method
outer side/
outer side
Surface Wetting Tension mN/m inner side 38 JIS Z1712
outer side 38
Surface Resistivity LogΩ • cm inner side 11 Toray Method
outer side 11

*Atomospheric Condition 25 °C65%RH

Applications

Packages for powder products (dried fish flakes, granular medicines, etc.)Adhesive tapes

Attention
1. We accept no responsibility for results obtained by the application of the information indicated and for the safety and suitability of the products, by itself or in combination with other products. Users are advised to perform their own tests to determine the safety and suitability of such product and product combinationaccording to each of its purposes.
2. Refer to our MSDS (Material Safety Data Sheet) before use.
3. The publication is not to be taken as a license to operate under, or as a recommendation to infringe any patents.
  • Back
  • Print Friendly Page

PAGE TOP

  • Terms of use
  • Privacy Policy
  • Site map

2548 TORAYFAN*

TORAYFAN*

Features

A biaxially oriented polypropylene film, both sides treated with corona discharge and having strong anti-static property.

1)Both sides of film excel in anti-static property .Best suited to uses in packaging for powder products.
2)As both sides have been treated with corona discharge, when it is processed into bags, the outer side of the bag will have superior adhesion property thus can be easily marked with data stamps and other marks.
3)The strength of the biaxially oriented polypropylene film and the corona discharge treatment given on both sides makes 2548 ideal for use in adhesive tapes.

Thickness

20,25,30,40,60µm

Typical properties

Properties Unit
Direction
/Side
Typical Data Measurement method
Tensile Strength MPa MD 140 JIS Z1712
TD 300
Elongation at Break % MD 190 JIS Z1712
TD 60
Young's Modulus GPa MD 1.8 ASTM D882-64T
TD 3.4
Thermal Shrinkage
(120°C 15min)
% MD 3.5 JIS Z1712
TD 0.0
Haze % - 2 JIS Z1712
Coefficient of Friction
(µs/µd)
- inner side/
inner side
0.25/0.20 Toray Method
outer side/
outer side
Surface Wetting Tension mN/m inner side 38 JIS Z1712
outer side 38
Surface Resistivity LogΩ • cm inner side 11 Toray Method
outer side 11

*Atomospheric Condition 25 °C65%RH

Applications

Packages for powder products (dried fish flakes, granular medicines, etc.)Adhesive tapes

Attention
1. We accept no responsibility for results obtained by the application of the information indicated and for the safety and suitability of the products, by itself or in combination with other products. Users are advised to perform their own tests to determine the safety and suitability of such product and product combinationaccording to each of its purposes.
2. Refer to our MSDS (Material Safety Data Sheet) before use.
3. The publication is not to be taken as a license to operate under, or as a recommendation to infringe any patents.

Print