2500H TORAYFAN*

Features

A biaxially oriented polypropylene film excelling in transparency and surface gloss.

1)Excellent in transparency
2)Excellent in mold release

Thickness

25,30,40,50,60µm

Typical properties

Properties Unit
Direction
/Side
Typical Data Measurement method
Specific Gravity     0.91 JIS K6758
Melting Point °C   165  
Tensile Strength MPa MD 150 JIS Z1712
TD 300
Elongation at Break % MD 200 JIS Z1712
TD 50
Young's Modulus GPa MD 1.8 ASTM D882-64T
TD 3.3
Falling Ball Impact Strength J/mm   67 JIS K6717
Tear Propagating Strength mN/m MD 2450 JIS Z1702
mN/m(g/mm) TD 1370(140)
Thermal Shrinkage
(120°C 15min)
% MD 2.5 JIS Z1712
TD 0.0
Haze % - 2 JIS Z1712
Light Transmittance % - 92 JIS K6714
Gloss(60°- 60° ) % - 140 JIS K8741
Coefficient of Friction(µs/µd) - inner side/
inner side
0.40/0.35 Toray Method
outer side/
outer side
0.40/0.35
Surface Wetting Tension mN/m inner side 30< JIS Z1712
outer side 30<
Volume Resistivity Ω • cm - 6×1018 JIS C2330
Coefficient of Water Vapor Transmission g • 0.1mm/m²,
24hr
- 1.5 JIS K6782
Coefficient of Oxygen Transmission cc • 0.1mm/m²,
24hr, atm
- 400 JIS Z1707

*Atomospheric Condition:25°C65%RH

Applications

Free-format/size photo albums, Mold release applications, Cable cover, Hot wire sealing(for textile-use and other packages)

Attention
1. We accept no responsibility for results obtained by the application of the information indicated and for the safety and suitability of the products, by itself or in combination with other products. Users are advised to perform their own tests to determine the safety and suitability of such product and product combinationaccording to each of its purposes.
2. Refer to our MSDS (Material Safety Data Sheet) before use.
3. The publication is not to be taken as a license to operate under, or as a recommendation to infringe any patents.
  • Back
  • Print Friendly Page

PAGE TOP

  • Terms of use
  • Privacy Policy
  • Site map

2500H TORAYFAN*

TORAYFAN*

Features

A biaxially oriented polypropylene film excelling in transparency and surface gloss.

1)Excellent in transparency
2)Excellent in mold release

Thickness

20,25,30,40,60µm

Typical properties

Properties Unit
Direction
/Side
Typical Data Measurement method
Specific Gravity     0.91 JIS K6758
Melting Point °C   165  
Tensile Strength MPa MD 150 JIS Z1712
TD 300
Elongation at Break % MD 200 JIS Z1712
TD 50
Young's Modulus GPa MD 1.8 ASTM D882-64T
TD 3.3
Falling Ball Impact Strength J/mm   67 JIS K6717
Tear Propagating Strength mN/m MD 2450 JIS Z1702
mN/m(g/mm) TD 1370(140)
Thermal Shrinkage
(120°C 15min)
% MD 2.5 JIS Z1712
TD 0.0
Haze % - 2 JIS Z1712
Light Transmittance % - 92 JIS K6714
Gloss(60°- 60° ) % - 140 JIS K8741
Coefficient of Friction(µs/µd) - inner side/
inner side
0.40/0.35 Toray Method
outer side/
outer side
0.40/0.35
Surface Wetting Tension mN/m inner side 30< JIS Z1712
outer side 30<
Volume Resistivity Ω • cm - 6×1018 JIS C2330
Coefficient of Water Vapor Transmission g • 0.1mm/m²,
24hr
- 1.5 JIS K6782
Coefficient of Oxygen Transmission cc • 0.1mm/m²,
24hr, atm
- 400 JIS Z1707

*Atomospheric Condition:25°C65%RH

Applications

Free-format/size photo albums, Mold release applications, Cable cover, Hot wire sealing(for textile-use and other packages)

Attention
1. We accept no responsibility for results obtained by the application of the information indicated and for the safety and suitability of the products, by itself or in combination with other products. Users are advised to perform their own tests to determine the safety and suitability of such product and product combinationaccording to each of its purposes.
2. Refer to our MSDS (Material Safety Data Sheet) before use.
3. The publication is not to be taken as a license to operate under, or as a recommendation to infringe any patents.