2248 TORAYFAN*

Features

A high-gloss and highly transparent biaxially oriented polypropylene film, excelling in blocking-and scratch-resistance, and suitable for print lamination.

1)Appearance
Excels in transparency and gloss, and brings out the best of printing and gives neat finished look.
2)Scratch-resistance(anti-wear)
Scratch-resistance has improved greatly, thus 2248 maintains its neat appearance and gloss quality even under the most demanding application conditions.
3)Handling property
It provides the same ease for post-processing, including lamination, as the conventional types.

Thickness

15µm

Typical properties

Properties Unit
Direction
/Side
Typical Data Measurement method
Tensile Strength MPa MD 150 JIS Z1712
TD 320
Elongation at Break % MD 180 JIS Z1712
TD 50
Haze(8sheets) % - 14 JIS Z1712
Gloss(60°- 60°) %   150 JIS K8741
Coefficient of Friction(µs/µd) - inner side/
inner side
0.25/0.20 Toray Method
outer side/
outer side
Surface Wetting Tension mN/m inner side 36 JIS Z1712
outer side
Scratch Resistance
Friction between 2 sheets
200g, 20 times.
% Before 2.7 Toray Method
After 3.3
Difference 0.6
Fish Eye piece/m² 500µm 2 Toray Method
piece/m² 400µm - 5
piece/m² 300µm - 40

*Atomospheric Condition 25°C65%RH

Applications

Print lamination (solvent bonding)

Attention
1. We accept no responsibility for results obtained by the application of the information indicated and for the safety and suitability of the products, by itself or in combination with other products. Users are advised to perform their own tests to determine the safety and suitability of such product and product combinationaccording to each of its purposes.
2. Refer to our MSDS (Material Safety Data Sheet) before use.
3. The publication is not to be taken as a license to operate under, or as a recommendation to infringe any patents.
  • Back
  • Print Friendly Page

PAGE TOP

  • Terms of use
  • Privacy Policy
  • Site map

2248 TORAYFAN*

TORAYFAN*

Features

A high-gloss and highly transparent biaxially oriented polypropylene film, excelling in blocking-and scratch-resistance, and suitable for print lamination.

1)Appearance
Excels in transparency and gloss, and brings out the best of printing and gives neat finished look.
2)Scratch-resistance(anti-wear)
Scratch-resistance has improved greatly, thus 2248 maintains its neat appearance and gloss quality even under the most demanding application conditions.
3)Handling property
It provides the same ease for post-processing, including lamination, as the conventional types.

Thickness

15µm

Typical properties

Properties Unit
Direction
/Side
Typical Data Measurement method
Tensile Strength MPa MD 150 JIS Z1712
TD 320
Elongation at Break % MD 180 JIS Z1712
TD 50
Haze(8sheets) % - 14 JIS Z1712
Gloss(60°- 60°) %   150 JIS K8741
Coefficient of Friction(µs/µd) - inner side/
inner side
0.25/0.20 Toray Method
outer side/
outer side
Surface Wetting Tension mN/m inner side 36 JIS Z1712
outer side
Scratch Resistance
Friction between 2 sheets
200g, 20 times.
% Before 2.7 Toray Method
After 3.3
Difference 0.6
Fish Eye piece/m² 500µm 2 Toray Method
piece/m² 400µm - 5
piece/m² 300µm - 40

Applications

Print lamination (solvent bonding)

Attention
1. We accept no responsibility for results obtained by the application of the information indicated and for the safety and suitability of the products, by itself or in combination with other products. Users are advised to perform their own tests to determine the safety and suitability of such product and product combinationaccording to each of its purposes.
2. Refer to our MSDS (Material Safety Data Sheet) before use.
3. The publication is not to be taken as a license to operate under, or as a recommendation to infringe any patents.

Print