Lumirror* Low Shrinkage type  (Off-line annealed)

Features

X60 series are films with low thermal shrinkage achieved by annealing Lumirror off-line.

Thickness

Depending on the base film.(Please contact us.)

Typical properties

Base film conditions 150°C/30min
MD0.5%
TD± 0.2%
180°C/30min
MD0.5%
TD± 0.2%
S type (S10,S105) X60K X60
H type (H10) X61K -
T type (T60) X62K X62

Applications

All applications requiring low thermal shrinkage

Attention
1. We accept no responsibility for results obtained by the application of the information indicated and for the safety and suitability of the products, by itself or in combination with other products. Users are advised to perform their own tests to determine the safety and suitability of such product and product combinationaccording to each of its purposes.
2. Refer to our MSDS (Material Safety Data Sheet) before use.
3. The publication is not to be taken as a license to operate under, or as a recommendation to infringe any patents.
  • Back
  • Print Friendly Page

PAGE TOP

  • Terms of use
  • Privacy Policy
  • Site map

Lumirror* Low Shrinkage type  (Off-line annealed)

Polyester Film Lumirror*

Features

X60 series are films with low thermal shrinkage achieved by annealing Lumirror off-line.

Thickness

Depending on the base film.(Please contact us.)

Typical properties

Base film conditions 150°C/30min
MD0.5%
TD± 0.2%
180°C/30min
MD0.5%
TD± 0.2%
S type (S10,S105) X60K X60
H type (H10) X61K -
T type (T60) X62K X62

Applications

All applications requiring low thermal shrinkage

Attention
1. We accept no responsibility for results obtained by the application of the information indicated and for the safety and suitability of the products, by itself or in combination with other products. Users are advised to perform their own tests to determine the safety and suitability of such product and product combinationaccording to each of its purposes.
2. Refer to our MSDS (Material Safety Data Sheet) before use.
3. The publication is not to be taken as a license to operate under, or as a recommendation to infringe any patents.

Print